| pH. |
7.0 ASTM D 2369 |
| Water Immersion |
168 hours, coating unchanged. ASTM D 870 |
| Salt spray resistance |
240 hours with a 3 mil dry film thickness. |
| Freeze thaw resistance: |
1 hr. at -120 F 1 hr. -5-F 1 hr. 70-75 F no v |
| Adhesion test |
500 PSI to rusted metal and using top coat of
2 component solvent base epoxy has the same resistance. Elcometer
pull test. |
| X Ray diffraction |
Product changes rust from active to passive stage. |
| Heat resistance |
Up to 230 F. ASTM D 2485. |
| Dielectric Strength |
Strength is 186 volts/mil. Breakdown 1320 volts.
ASTM D 149. |
| Flexibility |
No cracking when bent over 1/8" mandrel
through 180 ASTM D 1737. |
| VOC Maximum |
0.25 Lb. per Gal. 30 Grams per Liter. ASTM D
396. |
| Coverage |
900 square feet per gallon at 1 mil dry film
thickness, depending on roughness and porosity of the surface.
Leneta T. G. logicator standard. |
| Composition |
Water emulsion, and water soluble polymers. |
| Chemical Exposure |
(A) 5% Hcl 24 Hrs. (B) 5% NaoH 24 Hrs. No deleterious
effects were observed following these exposures. ASTM D 1308. |
| Solvent resistance |
| (A) Ms. 1008 |
(B) 60% volume petroleum naphtha
25% volume toluene
15% volume Xylene. |
After 4 week exposure the coatings on the panels did not
soften or change in appearance. ASTM D 381. |
| Viscosity |
82-87 KU. |
| Weight per gallon |
10.7 lbs. minimum. |
| Total solids |
45.71 minimum per weight of paint. ASTM D 2369 |
| * Drying time |
To touch, half-hour maximum. |
| Through dry |
2-3 hours. |
| ** To top coat |
4 hours, depending on environmental conditions. |
| Solvent |
None. |
| Flash Point |
None |
| Grind |
6-7 Hegman. |
| Pigment |
Does NOT contain lead, chrome, or other toxic
pigments. |
| Corrosion deposits |
Results of salt spray test ASTM B 117 will prove
there could be no evidence of corrosion. |
| * Drying, curing time : |
At 77°F and 50% humidity with 3 mils dry film
thickness. |
FURTHER INFORMATION.
For further information, please contact our technical department.